Eigenschaften | Einheiten | Oxide | Nichtoxide | Bearbeitbare Materialien | ||||||||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Aluminiumoxid | ZTA | ATZ | Zirkonia | Aluminiumnitrid | Siliciumcarbid | Borcarbid | Siliziumnitrid | Bornitrid | Shapal Hi M Soft | Macor | ||||||||||||||||
96% | 99.7% | 99.95% | ZTA | Ultrahart | ATZ | Ultra Tough | 3YZ | PCAN1000 | PCAN2000 | PCAN3000 | PCAN4000 | Siliciumcarbid | Borcarbid | PCSN1000 | PCSN2000 | PCSN3000 | PCSN4000 | Klasse A | Klasse AX05 | Klasse HP | Klasse M26 | Klasse ZSBN | Shapal Hi M Soft | Macor | ||
Festigkeit Keramik | MPa | 2000 | 2000 | 3500 | 2500 | 3000 | 2500 | 2000 | 2000 | 3000 | 3000 | 3000 | 3000 | 2500 | 3000 | 3000 | 3000 | 3000 | 3000 | 143 ∥ / 186 ⊥ | 25 ∥ | 96 ∥ | N / A | 219 ∥ / 254 ⊥ | 980 | 345 |
Dichte | g/cm3 | 3.75 | 3.95 | 3.98 | 4.1 | 4.18 | 5.5 | 5.7 | 6.05 | 3.32 | 3.32 | 3.32 | 3.3 | 3.1 | 2.52 | 3.2–3.4 | 3.2–3.4 | 3.2–3.3 | 3.23 | 2.0 | 1.9 | 2.0 | 2.1 | 2.9 | 2.88 | 2.52 |
Biegefestigkeit bei 25°C | MPa | 200-300 | 250-350 | 500-600 | 600 | 850 | 1800 | 1000 | 1200 | 350 | 350 | 350 | 350 | 410 | 420 | 730 | 970 | 760–830 | 850 | 94 ∥ / 65 ⊥ | 22 ∥ / 21 ⊥ | 59 ∥ / 45 ⊥ | 62 ∥ / 34 ⊥ | 144 ∥ / 107 ⊥ | 300 | 94 |
Bruchzähigkeit K IC | MPa m1/2 | 4.5 | 4 | 4.5 | 7 | 5 | 8 | 17 | 8 | 3 | 3 | 3 | 2.5 | 4.6 | 2.5 | 7.0 | 6.2 | 6,2–6,5 | 8.5 | N / A | N / A | N / A | N / A | N / A | 2 | 1.5 |
Härte | GPa | 12 | 14 | 18 | 16 | 21.5 | 14 | 13 | 13.5 | 10 | 10 | 10 | 12 | 28 | 33 | 15 | 15 | 15.3-15-6 | 16 | N / A | N / A | N / A | N / A | N / A | 3.8 | 2.3 |
Elastizitätsmodul | GPa | 300 | 370 | 400 | 335 | 350 | 340 | 200 | 200 | 300-350 | 300-350 | 300-350 | 300-350 | 350-400 | 350-450 | 300 | 300 | 300–310 | 340 | 47 ∥ / 74 ⊥ | 17 ∥ / 71 ⊥ | 40 ∥ / 60 ⊥ | N / A | 71 ∥ / 71 ⊥ | 176 | 66.9 |
Wärmeleitfähigkeit bei 25 °C | W/mK | 25 | 33 | 45 | 20 | 20 | 6 | 3 | 2 | 170 | 200 | 230 | 200 | 102.6 | 20-40 | 25 | 24 | 25 | 28 | 30 ∥ / 34 ⊥ | 78 ∥ / 130 ⊥ | 27 ∥ / 29 ⊥ | 11 ∥ / 29 ⊥ | 24 ∥ / 34 ⊥ | 92 | 1.5 |
WAK bei 25 °C – 400 °C | 10-6/K | 6.3 | 6.5 | 7.5 | 7 | 7.5 | 8 | 10 | 10 | 4.5 | 4.5 | 4.5 | 3.5 | 4.02 | 90 | 2.5 | 2.5 | 2.5 | 2.5 | 3 ∥ / 3 ⊥ | -2,3 ∥ / -0,7 ⊥ | 0,6 ∥ / 0,4 ⊥ | 3 ∥ / 0,4 ⊥ | 4,1 ∥ / 3,4 ⊥ | 4.8 | 9 |
Max. Temperatur (Luft) | °C | 1600 | 1700 | 1750 | 1500 | 1500 | 1200 | 800 | 800 | 1200 | 1200 | 1200 | 1200 | 1200 | N / A | 1200 | 1200 | 1200 | 1200 | 850 | 850 | 850 | 1000+ | 850 | 1000 | 800 |
Max. Temperatur (inert) | °C | 1600 | 1700 | 1750 | 1500 | 1500 | 1200 | 1500 | 1000 | 1200 | 1200 | 1200 | 1200 | 1900 | 1800 | 1400 | 1400 | 1400 | 1400 | 1200 | 2000 | 1150 | 1000+ | 1600 | 1900 | 1000 |
Dielektrizitätskonstante bei 1 MHz | – | 9.8 | 9.9 | 9.9 | 10 | 10 | 25 | 29 | 29 | 8.8 | 8.8 | 8.5 | 8.5 | N / A | 5-8 | 8 | 8 | 8 | 7 | 4,6 ∥ / 4,2 ⊥ | 4,0 ∥ / 4,0 ⊥ | 4,3 ∥ / 4,0 ⊥ | 4,5 ∥ / 3,8 ⊥ | 18 ∥ / 19 ⊥ | 6.8 | 6 |
Durchschlagsfestigkeit (DC) | kV/mm | 9 | 11 | 16 | 16 | 16 | 16 | 18 | 18 | 15 | 15 | 15 | 15 | N / A | N / A | 19 | 19 | 19 | 19 | 88 | 79 | 10 | 66 | 3.5 | 65 | 62 |
Volumenwiderstand bei 25 °C | Ohm-cm | >1014 | >1014 | >1016 | >1016 | >1016 | >1016 | >1012 | >1012 | >1013 | >1013 | >1013 | >1014 | 102–1011 | N / A | >1014 | >1014 | >1014 | >1012 | >10 13 ∥ /> 10 14 ⊥ | >10 13 ∥ /> 10 14 ⊥ | >10 13 ∥ /> 10 13 ⊥ | >10 13 ∥ /> 10 14 ⊥ | >10 13 ∥ /> 10 12 ⊥ | >1015 | >1016 |
Haftungsausschluss: Die angegebenen Werte sind Durchschnittswerte und typische Werte, die aus Testproben ermittelt wurden. Sie dienen lediglich als Anhaltspunkt für die Konstruktion von Keramikkomponenten und sind in keiner Weise garantiert. Die tatsächlichen Werte können je nach Form und Größe der vorgesehenen Komponente variieren.