Green Machining of Technical Ceramics – The More Economical Route

by | Oct 12, 2015

Green Machining

The machining of technical ceramics in an unfired state is called, quite simply, ‘green machining’ and in the case of some of the hardest ceramics, it is a far more economical route to take than post machining after firing.

In a typical process, a technical ceramic in powder form is mixed with an organic binder and then pressed at very high pressure into a pre-engineered mold to form a raw shape. At this stage, the ceramic is usually stable enough to machine as closely as possible to its finished state. The right choice of binder is, of course, very important and will have a major influence on machining at this green stage including the cutting suitability and mechanical resistance.

Careful calculation and allowance for shrinkage during firing must also be taken into consideration but this is often a much easier route to take than machining after firing when the ceramic becomes so hard and dense that only a minimum amount of grinding and shaping is possible.

Depending on the type of ceramic being manufactured, most types of common machining processes can be employed to turn the pressed ceramic into something a little closer to the end product. Precision Ceramics has extensive in-house machining facilities including 4th and 5th axis machining centres to cater for this. But whilst cutting, milling and grinding may be easy operations to carry out at the green stage, more precise drilling and hard grinding may have to wait until firing is complete or, in some applications, at the biscuit stage, when the ceramic is not fully sintered but significantly harder than at the green stage.

Right: Green machining of technical ceramics is an everyday process at Precision Ceramics.


In order for a technical ceramic to become hard and dense, it must be sintered or fired to high temperatures for prolonged periods of time in tightly controlled gas or electric kilns. Typical firing temperatures for alumina and zirconia range from 1,500°C to 1,800°C. Typical firing cycles vary between 12 and 24 hours depending upon the kiln type and product.

In general ceramics shrink approximately 20% during the sintering process. Non-uniform shrinkage as a result of standard forming and machining processes can cause the ceramic to deform but the in-house knowledge and experience we have gained over many years will always ensure that such problems are kept to an absolute minimum and that the geometric accuracy of the component is maintained as closely as possible.

Post Firing

Once the sintering process is complete and the ceramic has cooled to a workable temperature, several different finishing processes can be employed to achieve the tight tolerances and surface finishes often demanded of bespoke technical ceramic components.

Of these, precision grinding is the most common but through the careful control of the firing process, this is generally kept to minimum due to the extreme hardness of the now fully sintered ceramic. At this stage is it also usually possible to drill and tap the ceramic component if required.

Most fired aluminas can also become dirty through handling, machining and inspection procedures but can be easily cleaned using a variety of effective techniques.

Biscuit Machining

Approximately half way through the sintering process, the green ceramic reaches a ‘biscuit’ state where almost all of the organic binder used in the original mix and pressing will have burnt off leaving an almost pure but not fully sintered material. At this stage, the ceramic is much harder than it was when ‘green’ and some of the machining operations that were not possible at the initial green stage may now be practical – tapping and threading for instance.

Of course, there will still be shrinkage in the final sintering process but again, this can be calculated and controlled to get the best end results.

Interested in finding out more and if any of our materials are the right fit for your application? Please don’t hesitate to get in touch.

Related topics:

Ceramics Machining & Grinding

Precision Ceramics has extensive experience with high-tolerance advanced ceramic milling, grinding and polishing of unfired (‘green’) and fired ceramics.

Advanced Ceramic Manufacturing

Precision Ceramics is internationally renowned as as one of the world’s authorities in custom ceramic component engineering & design support.

Most Recent Posts

Wear Resistant Ceramics: Sliding, Abrasion & Impact

Wear Resistant Ceramics: Sliding, Abrasion & Impact

How do ceramic materials perform against sliding, abrasive or impact wear?Ceramics are inherently very wear resistant due to their extreme hardness; these materials have values close to the hardest known material, diamond. They have also the capability to be machined...

Exploring the Different Types of Nuclear Fusion

Exploring the Different Types of Nuclear Fusion

The quest for achieving practical nuclear fusion has driven the exploration of various types of fusion, each offering a distinct methodology and holding its own promise for future energy production. At its core, nuclear fusion involves the merging of two light atomic...

Ceramic Manufacturing Process: Quantity, Design and Cost

Ceramic Manufacturing Process: Quantity, Design and Cost

How does quantity influence tooling costs and the ceramic manufacturing process?Quantity can be a game-changer in the ceramic manufacturing process. When you're making large quantities of ceramics, prices tend to drop, as with any other product. And that's when it...